Hard-surfacing

硬

面

堆

焊

D 667

EDZCr-B-15

HRc≥48. Resistance to wear, gas corrosion and oxidation. Hardfacing of blast furnace hopper and cracker part.
HRc≥48，耐磨、耐氣蝕、抗氧化。堆焊高(gāo)爐料鐘(zhōng)、破碎機件

D 802

EDCoCr-A-03

HRc38-47. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as the edge of thermo-cutter.
HRc38-47，耐熱、耐蝕、耐磨。堆焊高(gāo)溫工(gōng)件如熱剪切刀(dāo)刃

ECoCr-A

D 812

EDCoCr-B-03

HRc45-50. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as internal-combustion engine valve.
HRc45-50，耐熱、耐蝕、耐磨。堆焊高(gāo)溫工(gōng)件如内燃機閥

ECoCr-B

D 822

HRc≥53. Resistance to Wear and heat, bad shock resistance. Hardfacing of rotating blade wheel of boiler.
HRc≥53，耐熱、耐磨，但(dàn)抗沖擊性差。堆焊鍋爐旋轉葉輪

D 832

EDCoCr-C-03

HRc≥50. Wear and heat resistance. Hardfacing of high temperature part such as hot-rolling guided way.
HRc≥50，耐熱、耐磨。堆焊高(gāo)溫工(gōng)件如熱軋導軌

ECoCr-C

D 842

EDCoCr-D-03

HRc28-38. Corrosion and thermo-fatigue resistance, work harding. Hardfacing of hot forging die.
HRc28-38，耐蝕、抗熱疲勞，具有加工(gōng)硬化性。堆焊熱鍛模

Cast iron

鑄

鐵(tiě)

Z 308

EZNi

Pure nickel, excellent general properties. Used to weld thin cast iron part and repair welding machined surface, such as guided way of machine tool.
純鎳，綜合性能(néng)好(hǎo)。鑄鐵(tiě)薄件及加工(gōng)面補焊用(yòng)，如機床導衛

ENi-Cl

Z 408

EZNiFe

Iron nickel, high strength and excellent ductility. Repair welding of important gray cast iron and nodular cast iron, such as cylinder cap.
鎳鐵(tiě)，強度高(gāo)、塑性好(hǎo)。重要灰鑄鐵(tiě)及球鐵(tiě)焊補用(yòng)，如汽缸蓋

ENiFe-Cl

Z 508

EZNiCu-1

Copper nickel, good machinability and bad crack resistance. Repair welding of sand hole and gray cast iron machined surface subject to no load.
鎳銅，易加工(gōng)，但(dàn)抗裂性較差。不受力的灰鑄鐵(tiě)加工(gōng)面及砂眼補焊

ENiCu-B

Copper alloys

銅

合

金(jīn)

Cu 107

ECu

Red copper, atmosphere and sea water corrosion and excellent electric conductivity. Welding of red copper such as electrical copper row.
紫銅，耐大(dà)氣，海水(shuǐ)腐蝕，導電性好(hǎo)。紫銅焊接用(yòng)，如導電銅排

ECu

Cu 207

ECuSi

Silicon bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass.
矽青銅，耐蝕、強度高(gāo)。銅、矽青銅及黃銅焊接用(yòng)

ECuSi

Cu 227

ECuSnB

Tin phosphor bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass.
錫磷青銅，耐蝕、強度高(gāo)。銅、矽青銅及黃銅焊接用(yòng)

ECuSn-C

Cu 237

ECuAl

Aluminum bronze, wear and corrosion and high strength. Welding or surfacing of copper alloys.
鋁青銅，耐磨、耐蝕，強度高(gāo)。銅合金(jīn)焊接或堆焊用(yòng)

ECuAl-A2

Aluminum alloys

鋁

合

金(jīn)

Al 109

TAl

Pure aluminum, excellent corrosion resistance and middle strength. Welding of pure aluminum.
純鋁，耐蝕性好(hǎo)，但(dàn)強度不高(gāo)，純鋁焊接用(yòng)

E1100

Al 209

TAlSi

Silicon aluminum, good crack resistance and wide range of usage. Welding of aluminum alloys other than aluminum magnesium alloys.
鋁矽，抗裂性好(hǎo)，通用(yòng)性大(dà)。鋁合金(jīn)焊接用(yòng)，不宜焊接鋁鎂合金(jīn)

E4043

Al 309

TAMn

Manganese aluminum, corrosion resistance and high strength. Welding of aluminum alloys.
鋁錳，強度高(gāo)，耐蝕。鋁合金(jīn)焊接用(yòng)

E3003

Nickel alloys

鎳合金(jīn)

Ni 102

ENi-1

Pure nickel. Welding and surfacing of nickel and nickel to steel.
純鎳，用(yòng)于鎳、鎳與鋼的焊接與堆焊

ENi-1

Ni 207

ENiCu-7

Copper nickel. Welding and surfacing of copper nickel and copper nickel to steel.
鎳銅，用(yòng)于鎳銅、鎳銅與鋼的焊接與堆焊

ENiCu-7

Hardfacing

硬

面

堆

焊

S 101

C3 Cr28 Ni4
Si3.5 Fe Rem.

HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.
HRc48-54，耐磨、耐氣蝕、抗氧化。堆焊鏟鬥齒，泵套

S 111

C1 Cr29 W5
Co Rem.

HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.
HRc38-47，高(gāo)溫下(xià)耐磨、耐蝕。堆焊高(gāo)溫高(gāo)壓閥門(mén)

ECoCr-A

S 112

C1.5 Cr29 W8
Co Rem.

HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.
HRc45-50，高(gāo)溫下(xià)耐磨、耐蝕。堆焊閥門(mén)，熱軋孔型

ECoCr-B

S 113

C2.5 Cr30 W17
Co Rem.

HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.
HRc≥55，高(gāo)溫下(xià)耐磨、耐熱，但(dàn)抗沖擊性差。堆焊螺旋送料機用(yòng)

S 114

C2.5 Cr30 W12
Co Rem.

HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.
HRc≥53，高(gāo)溫下(xià)耐磨、耐熱，但(dàn)抗沖擊較差。堆焊牙輪鑽頭

ECoCr-C

Copper

alloys

銅

合

金(jīn)

S 201

Sn1 Si0.3Mn0.3
Cu Rem.

Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
機械性能(néng)好(hǎo)，抗裂性好(hǎo)。紫銅氣焊及氩弧焊用(yòng)

ERCu

S 211

Si3 Mn1
Cu Rem.

Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.
機械性能(néng)好(hǎo)，銅合金(jīn)氩弧焊及鋼的MIG釺焊用(yòng)

ERCuSi-Al

S 212

Sn5 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好(hǎo)。銅合金(jīn)氩弧焊及鋼的堆焊用(yòng)

ERCuSn-A

S 213

Sn8 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好(hǎo)。銅合金(jīn)氩弧焊及鋼的堆焊用(yòng)

ERCuSn-C

S 214

Al7.5 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蝕。銅合金(jīn)氩弧焊及鋼的堆焊用(yòng)

ERCuAl-A1

S 215

Al9 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蝕。銅合金(jīn)氩弧焊及鋼的堆焊用(yòng)

ERCuAl-A2

S 221

Cu60 Sn1 Si0.3
Zn Rem.

Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點約890℃。黃銅氣焊及碳弧焊用(yòng)，也(yě)可釺焊銅、鋼、鑄鐵(tiě)

S 221F

Cu60 Sn1 Si 0.3
Zn Rem.

S221 welding rod coated with flux.
外(wài)塗焊劑的S221焊絲

S 222

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點約880℃。黃銅氣焊及碳弧焊用(yòng)，也(yě)可釺焊銅、鋼、鑄鐵(tiě)

RBCuZn-C

S 222F

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

S222 welding rod coated with flux.
外(wài)塗焊劑的S222焊絲

RBCuZn-C

S 223

Cu59 Sn0.6
Zn Rem.

Melting point is about 900℃. Braze welding of copper, steel and cast iron.
熔點約900℃。銅、鋼、鑄鐵(tiě)釺焊用(yòng)

RBCuZn-A

S 224

Cu62 Si0.5
Zn Rem.

Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點約905℃。黃銅氣焊及碳弧焊用(yòng)，也(yě)可釺焊銅、鋼、鑄鐵(tiě)

Copper
alloys

銅

合

金(jīn)

S 225

Cu48 Ni10
Zn Rem.

Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys.
熔點約935℃。高(gāo)強度,釺焊鋼、鎳及硬質合金(jīn)用(yòng)

RBCuZn-D

S 225F

Cu48 Ni10
Zn Rem.

S225 welding rod coated with flux.
外(wài)塗焊劑的S225焊絲

RBCuZn-D

S 226

Cu60 Sn0.3
Si0.2 Zn Rem.

Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron.
熔點約900℃。黃銅氣焊用(yòng)，也(yě)可釺焊銅、鋼、鑄鐵(tiě)

S 227

Cu58Sn0.9Ni0.5
Si0.1 Fe0.8
Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點880℃。黃銅氣焊及碳弧焊用(yòng)，也(yě)可釺焊銅、鋼、鑄鐵(tiě)

RBCuZn-B

S 229

Cu55 Ni6 Mn4
Zn餘

Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide.
熔點約920℃。高(gāo)強度,釺焊鋼、鎳及硬質合金(jīn)用(yòng)

Aluminum alloys

鋁

合

金(jīn)

S 301

Al≥99.5

Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.
塑性好(hǎo)、耐蝕。純鋁氣焊、氩弧焊用(yòng)

ER1100

S 311

Si5 Al Rem.

Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.
抗裂性好(hǎo)，通用(yòng)性大(dà)。鋁合金(jīn)氣焊、氩弧焊用(yòng)。不宜用(yòng)高(gāo)鎂合金(jīn)

ER4043

S 321

Mn1.3 Al Rem.

Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.
良好(hǎo)的耐蝕性、可焊性及塑性。鋁合金(jīn)氣焊、氩弧焊用(yòng)

S 331

Mg5 Mn0.4
Al Rem.

Corrosion resistance and high strength. Argon arc welding of aluminum alloys.
耐蝕，強度高(gāo)。鋁合金(jīn)氩弧焊用(yòng)

ER5183